5CrNiMoV φ10 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ12 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ16 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ20 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ26 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ30 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ35 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ40 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ46 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ50 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ55 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ60 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ65 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ70 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ75 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ80 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ85 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ90 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ95 (軋材）高耐磨性熱鍛模具鋼
5CrNiMoV φ100 (鍛材）高耐磨性熱鍛模具鋼
5CrNiMoV φ110 (鍛材）高耐磨性熱鍛模具鋼
5CrNiMoV φ120 (鍛材）高耐磨性熱鍛模具鋼
5CrNiMoV φ130 (鍛材）高耐磨性熱鍛模具鋼
5CrNiMoV φ140 (鍛材）高耐磨性熱鍛模具鋼
5CrNiMoV φ150 (鍛材）高耐磨性熱鍛模具鋼
5CrNiMoV φ160 (鍛材）高耐磨性熱鍛模具鋼
5CrNiMoV φ170 (鍛材）高耐磨性熱鍛模具鋼
5CrNiMoV φ180 (鍛材）高耐磨性熱鍛模具鋼
5CrNiMoV φ190 (鍛材）高耐磨性熱鍛模具鋼
5CrNiMoV φ200 (鍛材）高耐磨性熱鍛模具鋼
金屬材料牌號：5CrNiMoV
鋼材種類：高耐磨性熱鍛模具鋼
化學成分：
C: 0.5~0.6
Si:≤0.35
Mn:0.5~0.8
P:≤0.03
S:≤0.03
Cr:0.8~1.1
Mo:0.35~0.5
Ni:1.4~1.8
V:0.1~0.3
主要特點
冶煉特點
成分設計特點：韌性好、強度高、耐磨性好。
采用電弧爐（EAF）+精煉（LF）+真空（VD）生產的模具鋼純凈度高、性能好。
熱 處 理
退火：760-780℃ 硬度：197-241HB
淬火溫度：890-910℃，油冷，硬度：61.5HRC
回火溫度：420-550℃，回火兩次
硬度：38-47HRC
此鋼在空氣中冷卻即能淬硬，并易形成白點，因此鍛造后應緩慢冷卻。
對于大型鍛件，必須放到600℃的爐中，待溫度一致后，再緩慢冷卻到150-200℃，然后再在空氣中冷卻。
對于較大的鍛件，建議在冷卻到150-200℃以后，立即進行回火加熱。
性能優點和用途:優良的淬透性、強度高、優良的耐磨性.該種鋼用來制造各種大、中型鍛模。