Teflon? PTFE

TE3859/TE3893: General-purpose resin composed of 60% PTFE dispersed in water. Contains a nonionic wetting agent and stabilizer.( 通用樹脂組成的60％聚四氟乙烯分散在水中。包含非離子潤濕劑和穩定劑。)

TE3864: TE3864 replaces Teflon? PTFE B; aqueous dispersion containg 61%, by total weight, of active ingredients. Special formulation designed for application to woven glass fabric used to make bags for difficult gaseous filtration or product collection systems. Excellent hydrophobisity and chemical resistance(TE3864取代特富龍?聚四氟乙烯乙;水分散體總重的有效成分，containg61％。特殊配方設計中的應用玻璃纖維織物用于彌補困難氣體過濾袋或產品的收集系統。優秀hydrophobisity和耐化學性)

TE3875/TE3876: Good gloss, high shear stability and good weldability; improved abrasion resistance, flex-life and color. 60%  PTFE dispersed in water. Contains a nonionic wetting agent and stabilizer.( 光澤度好，高剪切穩定性和良好的可焊性，改善耐磨性，彈性，生命和顏色。 60％的聚四氟乙烯分散于水中。包含非離子潤濕劑和穩定劑)

TE3885/TE3908: Resin composed of approximately  61% PTFE dispersed in water. Contains a nonionic wetting agent and stabilizer.( 樹脂組成的約61％聚四氟乙烯分散在水中。包含非離子潤濕劑和穩定劑)

TE3890: Resin composed of nominal 35% PTFE dispersed in water with an anionic wetting agent.( 樹脂組成的名義35％聚四氟乙烯分散在水中的陰離子潤濕劑)

6C: General-purpose resin. Medium reduction ratio. Excellent color and clarity. Accepts filler exceptionally well.( 通用樹脂。中等縮小比例。出色的色彩和清晰度。接受填料出色)

60: Low reduction ratio. High-pressure resin.( 低減速比。高壓樹脂)

62: Premium resin offers highest thermal stability, stress crack resistance, flex life, and clarity of all grades. Low to medium reduction ratio.( 高級樹脂提供了最高的熱穩定性，耐應力開裂，彎曲的生活，和所有級別的清晰度。低到中等縮小比例)

601A: High molecular weight. Low reduction ratio. Excellent thermal stability.( 高分子量。低減速比。優良的熱穩定性)

602A: Low reduction ratio. Medium molecular weight. Excellent thermal stability.( 低減速比。中等分子量。優良的熱穩定性)

610A: Medium to high reduction ratio.( 中到高減速比)

613A: Low reduction ratio.( 低減速比)

CFP6000: High reduction ratio. Low-pressure resin.( 高壓縮比。低壓樹脂)

7A: Finely divided 35-micron particles. 460-g/L bulk density. Up to 5,500 psi in tensile strength. Maximum granular PTFE chemical resistance. Parts fabricated from this resin have excellent physical and electrical properties.( 精細分割35微米的顆粒。 460 g / L的體積密度。高達5500 psi的拉伸強度。最大顆粒聚四氟乙烯的耐化學性。這種樹脂制成的零件具有優異的物理和電氣性能)

7C: Finely divided "fluffy" 20-micron particles. 250-g/L bulk. Up to 5,900 psi in tensile strength. Often used in applications requiring excellent flex life. Parts fabricated from this resin have excellent physical and electrical properties.( 精細分割“蓬松“20微米的顆粒。 250 g / L的大部分。高達5,900 psi的拉伸強度。常用于要求具有出色的彈性生活中的應用。這種樹脂制成的零件具有優異的物理和電氣性能)

8A: Pelletized 510-micron particles. 690-g/L bulk density. Up to 4,480 psi in tensile strength. Resin particles are preformed using lower preform pressures. Parts fabricated from this resin have superior physical and electrical properties.( 球團510微米的顆粒。 690 g / L的體積密度。高達4,480 psi的拉伸強度。樹脂顆粒預制件預制使用較低的壓力。這種樹脂制成的零件具有優良的物理和電氣性能)

807-N: A multi-purpose PTFE resin which yields high productivity due to its high fill density. It has an excellent combination of handleability, processability, machinability and end-use properties.Note: Teflon? 807-N meets the requirements of ASTM D 4894-91a, type IV, grade 2 (except for tensile properties).( 多用途聚四氟乙烯樹脂產量高生產力，由于其高填充密度。它有一個可操作性，加工性能，可加工性和最終使用性能的完美結合。注：特富龍?807- N的符合美國ASTMe4894-91a，IV型的要求，2級（除拉伸性能）。)

NXT70: A fine-cut resin designed for compression molding of blocks and sheets and for use as a base resin for compounds.( 阿細切樹脂設計 縮成型塊和片并作為基礎樹脂的化合物的使用)

NXT75: A fine-cut resin designed for eneral compression molding of blocks and sheets and for use as a base resin for compounds.( 阿細切樹脂設計 和片并作為基礎樹脂使用的化合物一般壓縮成型)

NXT85: Chemically modified free-flow granular molding resin can be converted to parts by isostatic, billet, and sheet molding methods, as well as ram extrusion.( 化學改性的自由流動顆粒成型樹脂可轉換為以均衡，部分鋼坯和薄板成型方法，以及RAM的擠壓)